特點
● 低的Z軸熱膨脹系數(shù)，優(yōu)良通孔可靠性
● 優(yōu)良的PCT性能，低吸水率和耐高溫高濕性
● 優(yōu)良的機械加工性和耐熱性，無鉛兼容FR-4.0板材
應用領域
● 專為有耐熱性和耐CAF性能要求的汽車電子設計，也適用于高多層PCB- 產品性能
- 產品證書
- 資料下載
| Items | Method | Condition | Unit | Typical Value |
|---|---|---|---|---|
| Tg | 2.4.24.4 | DMA | ℃ | 185 |
| 2.4.25D |
DSC |
180 | ||
| Td | 2.4.24.6 | 5% wt. loss | ℃ | 355 |
|
T288 |
2.4.24.1 | TMA | min | 40 |
| T260 |
2.4.24.1 |
TMA |
min |
60 |
|
Thermal Stress |
2.4.13.1 |
288℃, solder dip |
- |
>100s No Delamination |
| CTE (Z-axis) | 2.4.24 | Before Tg | ppm/℃ | 40 |
| After Tg | ppm/℃ | 190 | ||
| 50-260℃ | % | 2.2 | ||
| Dissipation Constant (1GHz) | 2.5.5.9 | C-24/23/50 | - |
4.4 |
|
Dissipation Factor (1GHz) |
2.5.5.9 |
C-24/23/50 |
- | 0.012 |
| Volume Resistivity | 2.5.17.1 | C-96/35/90 | MΩ.cm | 8.12×108 |
|
Surface Resistivity |
2.5.17.1 |
C-96/35/90 | MΩ | 2.65×107 |
| Arc Resistance | 2.5.1 | D-48/50+D-0.5/23 | s | 135 |
| Dielectric Breakdown | 2.5.6 | D-48/50+D-0.5/23 | kV | 45+kV NB |
| Peel Strength (1Oz) | 2.4.8 | 288℃/10s | N/mm | 1.4 |
| Flexural Strength(LW/CW) | 2.4.4 | A | MPa | 560/440 |
| Water Absorption | 2.6.2.1 | E-1/105+D-24/23 | % | 0.07 |
|
Flammability |
UL94 |
C-48/23/50 |
Rating |
V-0 |
| CTI | IEC60112 | A | Rating | PLC 3 |
Remarks:
1. All the typical values are based on the 1.6mm specimen. Test method is according to IPC-TM-650.
2. All the typical values listed above are for your reference only and not intended for specification. Please contact Shengyi Technology Co., Ltd. for detailed information. All rights from this data sheet are reserved by Shengyi Technology Co., Ltd.
Explanation: C=Humidity conditioning, D=Immersion conditioning in distilled water, E=Temperature conditioning
The first digit following the letter indicates the duration of preconditioning in hours, the second digit the preconditioning temperature in ℃ and the third digit the relative humidity.